PPS BZ-G2B

20% glass fiber reinforced PPS

Product features

 This kind of product is one of the high performance enhanced polyphenylene sulfide (PPS) compounds series products manufactured by our company. It is made by mixing the glass fiber and related additives on the basis of PPS regins through the twin screw extruder. It has good mechanical properties, high rigidity, high resistance to creep, high temperature resistance, flame retardant, chemical corrosion resistance, excellent electrical insulation, good arc resistance, good processing performance, low molding shrinkage, good radiation, good dimensional stability and so on. It is especially suitable for processing thin-walled parts.


Product applications

Due to the outstanding features of this product, it is widely used in electronics and electronics industry, making connectors, connectors, frequency dividers and components and shells of various instruments and instruments; In the aerospace industry, high strength, high temperature, insulation and various high performance requirements are made. The production of precision electrical connector, high strength shell, high temperature resistance contactor, etc.

Product performance

Test Items   

Unit

Performance      

TeST Standard

Density

g/cm3

1.50

GB/T 1033

Molding Shrinkage

%

0.25/0.80

GB/T 15585

Water Absorption

%

0.02

GB/T 2914

Tensile Strength

MPa

115

GB/T 1040

Elongation at break

%

1.8

GB/T 1040

Bending Strength

MPa

180

GB/T 9341

Flexural Modulus

MPa

1.0×104

GB/T 9341

Notched izod impact strength

KJ/m2

8

GB/T 1843

Melting Point

280

GB/T 4608

Heat Distortion Temperature/ HDT(1.8MPa)

260

GB/T 1634

Volume Resistivity ×1015

Ω.m

5

GB/T 1410

Surface Resistivity ×1014

Ω

5

GB/T 1410

Permittivity 1MHz

/

4

GB/T 1409

Dielectric Strength

KV/mm

18

GB/T 1408

Flame Retardant

/

V-0

GB/T UL94

Conditions:

1. Material drying process

Temperature: 130 ~ 150 ℃ *4 hours

Note: if any metal insert molding products, need to preheat insert: metal insert preheating temperature: 130 ~ 140 ℃, time: constant temperature for 1 hour

2. Injection molding process

Mold temperature: 120 ~ 150 ℃ (can be set according to the product structure situation)

Cylinder temperature:

The front:290~300℃

In the middle:300~320℃

The last period:310~330℃

Nozzle:310~330℃

Injection pressure:80~150MPa(70-95%)

Injection speed: medium speed ~ high speed.

Pressure holding pressure: 30-70MPa (20-45%)

      Meter: the residual amount is set 5-10mm.

Loose back: 3-5 mm

Screw rotation speed: 50-120rpm.

Back pressure: 0.2-5MPa.

Injection molding time: according to the size of the parts, when the mold is filled with mold, and the surface is basically cooling is good.

3. Post-processing technology: determined by the size of the parts.

Processing temperature: 160 ~ 180 ℃, the processing time: 4 ~ 8 hours

 