PPS BZ-EG33B

Anti-static PPS

Product features

This kind of product is one of the anti-static modified polyphenylene sulfide (PPS) compounds manufactured by our company, it is made by mixing glass fiber, conductive materials and related additives on the basis of PPS resins. It has anti-static property, high temperature resistance,creep resistance, chemical corrosion, flame retardant and other characteristics. In addtion, it has good processing performance and low molding shrinkage.

Product applications

Because of its outstanding characteristics of antistaic property, it is widely used in the automotive, electronics, electrical appliances, electrical appliances, and chemical industries for making components for anti-staic requirements.

Product performance

 

Test Items

 

      Unit 

 

   Performance

 

  Test standard

Density

g/cm3

1.54

GB/T 1033

Molding Shrinkage

%

0.25/0.65

GB/T 15585

Water Absorption

%

0.02

GB/T 2914

Tensile Strength

MPa

110

GB/T 1040

Elongation at break

%

 0.8

GB/T 1040

Bending Strength

MPa

190

GB/T 9341

Flexural Modulus

MPa

0.9×104

GB/T 9341

Notched izod impact strength

KJ/m2

6.0

GB/T 1843

Melting Point

270

GB/T 4608

Heat Distortion Temperature/

HDT(1.8Mpa)


252

GB/T 1634

Insulation Resistance

Ω.cm

1×107

GB/T 1410

        Flame Retardant

/

V-0

GB/T UL94


Conditions:

1. Material drying process

Temperature: 130 ~ 150 ℃ *4 hours

Note: if any metal insert molding products, need to preheat insert: metal insert preheating temperature: 130 ~ 140 ℃, time: constant temperature for 1 hour

2. Injection molding process

Mold temperature: 120 ~ 150 ℃ (can be set according to the product structure situation)

Cylinder temperature:

The front: 280 ~ 290 ℃

In the middle: 290 ~ 300 ℃

The last period: 300 ~ 310 ℃

Nozzle: 290 ~ 310 ℃

Injection pressure: 80~150MPa (70-95%)

Injection speed: medium speed ~ high speed.

Pressure holding pressure: 30-70MPa (20-45%)

Meter: the residual amount is set 5-10mm.

Loose back: 3-5 mm

Screw rotation speed: 50-120rpm.

Back pressure: 0.2-5MPa.

Injection molding time: according to the size of the parts, when the mold is filled with mold, and the surface is basically cooling is good.

 

3. Post-processing technology: determined by the size of the parts.

Processing temperature: 160 ~ 180 ℃, the processing time: 4 ~ 8 hours

 

 