PPS BZ-G3

30% glass fiber reinforced PPS

Product features

This kind of product is one of the high cost performance enhanced polyphenylene sulfide series products manufactured by our company. It is mixed granulation by adding the glass fiber through the twin screw extruder on the basis of PPS resin.The comprehensive mechanical performance of this product is good, it has high stiffness and creep resistance, high temperature resistantance, flame retardant, resistance to chemical corrosion and electrical insulation properties, good arc resistance, low water absorption, etc. In addition, it has good processing performance, small molding shrinkage,  dimontional stability, resistance to radiation and other characteristics, suitable for high precision parts.

Product applications

Because of the comprehensive performance of this product, it is used in the aerospace industry to produce all kinds of high performance requirements for high temperature and insulation. Production of corrosion resistant valve and insulation devices in chemical industry; In the electronics industry, the production of precision electrical connector, high strength shell, high temperature resistance contactor, etc. In the electrical industry, make use of the harsh electric machine parts, terminals, switches; In the machinery industry, the high temperature, the size of the high - size shaft sleeve, piston ring.

Product performance

Test Items

Unit

Performance

Test Standard

Density

g/cm3

1.56

GB/T 1033

Molding Shrinkage

%

0.25/0.75

GB/T 15585

Water Absorption

%

0.02

GB/T 2914

Tensile Strength

MPa

150

GB/T 1040

Elongation at break

%

1.7

GB/T 1040

Bending Strength

MPa

230

GB/T 9341

Flexural Modulus

MPa

1.1×104

GB/T 9341

Notched izod impact strength

KJ/m2

12

GB/T 1843

Melting Point

280

GB/T 4608

Heat distortion temperature/

HDT(1.8Mpa)

262

GB/T 1634

Volume Resistivity ×1015

Ω.m

5

GB/T 1410

Surface Resistivity ×1014

Ω

5

GB/T 1410

Permittivity 1MHz

/

4

GB/T 1409

Dielectric Strength

KV/mm

16

GB/T 1408

        Flame Retardant      /        V-0

GB/T UL94

Conditions:

1. Material drying process

Temperature: 130 ~ 150 ℃ *4 hours

Note: if any metal insert molding products, need to preheat insert: metal insert preheating temperature: 130 ~ 140 ℃, time: constant temperature for 1 hour

2. Injection molding process

Mold temperature:120~150℃(can be set according to the product structure situation

Cylinder temperature:

The front:290~300℃

In the middle:300~320℃

The last period:310~330℃

Nozzle:310~330℃

Injection pressure:80~150MPa(70-95%)

Injection speedmedium speed ~ high speed

Pressure holding pressure:30-70MPa(20-45%)

Meter: the residual amount is set 5-10mm.

Loose back: 3-5 mm

Screw rotation speed: 50-120rpm.

Back pressure: 0.2-5mpa

Injection molding time: according to the size of the parts, when the mold is filled with mold, and the surface is basically cooling is good.

3. Post-processing technology: determined by the size of the parts.

Processing temperature: 160 ~ 180 ℃, the processing time: 4 ~ 8 hours

 